On the extremely low cycle fatigue behavior of the concrete reinforcing bar FeB44k steel

Update: 2012-10-02

Description

Under extreme seismic conditions, engineering structures experience small numbers of very large displacement cycles. Reinforcing bar steel properties under very large displacement cycle loading can be studied by means of low cycle fatigue (LCF) test. In this study, we developed a low cycle fatigue testing system, which enables to study the low cycle fatigue strength of concrete reinforcing steel bars in the extreme large strain field; under such conditions the number of reversal to failure is well below one hundred cycles. A further advantage of this system is represented by the fact that the specimen is subjected to bending deformation. The obtained extremely low cycle fatigue (ELCF) strength for B450C (FeB44k) steel ribbed bars was compared with the results from smooth bars in order to assess the effect of ribs on the extremely low cycle fatigue behavior; further smooth bars were also subjected to heat treatments different from Tempcore, or surface modified by shot peening or by atmospheric corrosion.

Comments

In Channel

Impiego dei sensori FBG per il monitoraggio di beni di interesse storico artistico

2012-10-0219:02

Studio del cedimento di una protesi ortopedica in titanio

2012-10-0212:38

Predicting fatigue lifetime of engineering components under variable amplitude multiaxial fatigue loading

2012-10-0215:17

$Investigation on brittle fracture in rounded V-notched structures by Finite Fracture Mechanics$

Investigation on brittle fracture in rounded V-notched structures by Finite Fracture Mechanics

2012-10-0215:50

Size and load effects on the biaxial fatigue resistance of holed components

2012-10-0212:19

On the extremely low cycle fatigue behavior of the concrete reinforcing bar FeB44k steel

2012-10-0217:24

Simulazione della delaminazione a fatica: confronto tra tecnica Virtual Crack Closure e modello di zona coesiva

2012-10-0215:58

Discussion of Models for LCF Small Crack Growth

2012-10-0213:16

Prove per la caratterizzazione della propagazione della frattura di tubi in condizioni di sollecitazione ...

2012-10-0214:53

Twin-Twin Interaction in Fe-Cr using Digital Image Correlation

2012-10-0214:40

Correlazione fra tenacità a frattura e comportamento tribologico di rivestimenti ceramici e cermet ...

2012-10-0211:51

A mechanical model for FRP-strengthened concrete beams in bending

2012-10-0215:27

$Numerical modelling of intergranular fracture in polycrystalline materials and grain size effects$

Numerical modelling of intergranular fracture in polycrystalline materials and grain size effects

2012-10-0117:17

Valutazione del Volume Critico mediante analisi numeriche e sperimentali

2012-10-0111:43

Significance of J and CTOD Estimation Procedures for Common Fracture Specimens and Extension to Structural Components

2012-10-0117:31

From initiation of cracks to fatigue propagation: the interest of cohesive zone models

2012-10-0133:01

Determination of the fatigue limit by semi static tests

2012-10-0113:37

Coupled interface-body nonlocal damage models for the analysis of FRP strengthening detachment from cohesive material

2012-10-0115:47

Structural changing and recovery under uniaxial deformation in an NiTi superelastic alloy

2012-10-0113:34

Effetto della biassialità sulla valutazione dell’integrità strutturale di componenti contenenti difetti

2012-10-0115:31

00:00

On the extremely low cycle fatigue behavior of the concrete reinforcing bar FeB44k steel

R. Roberti, G. Cornacchia, M. Faccoli

#box-pro-ellipsis-176106777902411{-webkit-line-clamp:2;}On the extremely low cycle fatigue behavior of the concrete reinforcing bar FeB44k steel

On the extremely low cycle fatigue behavior of the concrete reinforcing bar FeB44k steel

R. Roberti, G. Cornacchia, M. Faccoli

On the extremely low cycle fatigue behavior of the concrete reinforcing bar FeB44k steel